长期热暴露对含钨铌γ-TiAl合金疲劳及表面损伤容限的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-07-05
选取热暴露(700 ℃，10000 h)前、后的Ti-44.5Al-5Nb-1W-1B(摩尔分数，%)(5-1-1合金)，对其表面引入不同深度的缺口(0~800 μm)，研究热暴露对该材料的疲劳性能及缺口损伤容限的影响，以Kitagawa-Takahashi线图的形式对热暴露引起的疲劳强化、长裂纹扩展门槛值以及合金在热暴露影响下对表面损伤的容忍限度进行定量分析。
长期热暴露对含钨铌γ-TiAl合金疲劳及表面损伤容限的影响Effects of long-term thermal exposure on fatigue behavior and surface defect tolerance of W+Nb containing γ-TiAl alloy 选取热暴露(700 ℃，10000 h)前、后的Ti-44.5Al-5Nb-1W-1B(摩尔分数，%)(5-1-1合金)，对其表面引入不同深度的缺口(0~800 μm)，研究热暴露对该材料的疲劳性能及缺口损伤容限的影响，以Kitagawa-Takahashi线图的形式对热暴露引起的疲劳强化、长裂纹扩展门槛值以及合金在热暴露影响下对表面损伤的容忍限度进行定量分析。结果表明:热暴露导致的回火稳态良性效应大于合金显微组织出现脆化的有害效应，使得热暴露后无缺口样品出现疲劳强度提高，而α2层片分解和组织细化能适当提高疲劳长裂纹扩展门槛值。当在热暴露后引入缺口而无回火效应时，长期热暴露导致的组织脆化成为控制性因素，材料的缺口敏感性增加，表现为出现短缺口效应的尺寸范围在热暴露后明显增大。
Single edge through thickness notch of different depths (0-800 μm) was introduced to the surface of Ti-44Al-5Nb-1W-1B alloy (5-1-1 alloy) before and after the thermal exposure at 700 ℃ for 10000 h. The effects of thermal exposure on the fatigue behaviour and the surface defect tolerance capability were studied. The exposure-induced fatigue strengthening, the fatigue threshold of long cracks and the surface defect tolerance under thermal exposure were quantitatively analysed and discussed in the form of Kitagawa-Takahashi diagram. The results show that the positive effect of the thermal exposure-induced tempering stability is greater than the harmful effect of the microstructural embrittlement. The fatigue strength of the non-notched is therefore improved after thermal exposure. On the other hand, the increase in threshold stress for long fatigue crack growth after the long-term exposure is attributed to the refinement of α2 lamellae. The introduction of the short notches after thermal exposure (hereby no tempering effect) has caused increased notch sensitivity, causing an increased notch size range within which the fatigue strength decreases significantly, due to microstructural embrittlement induced by the long-term thermal exposure.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.